The physicochemical properties of organo-silica xerogels derived from organo catalyst were pervasively investigated, including the effect of one-step catalyst (citric acid) and two-step catalyst (acid-base), and also to observe the effect of sol pH of organo-silica xerogel toward the structure and deconvolution characteristic. The organo-silica xerogels were characterized by FTIR, TGA and nitrogen sorption to obtain the physicochemical properties. The silica sol-gel method was applied to processed materials by employing TEOS (tetraethyl orthosilicate) as the main precursor. The final molar ratio of organo-silica was 1:38:x:y:5 (TEOS:ethanol: citric acid: NH3:H2O) where x is citric acid concentration (0.1-10 × 10-2 M) and y is ammonia concentration (0 to 3 × 10-3 M). FTIR spectra shows that the one-step catalyst xerogel using citric acid was handing over the higher Si-O-Si concentration as well as Si-C bonding than the dual catalyst xerogels with the presence of a base catalyst. The results exhibited that the highest relative area ratio of silanol/siloxane were 0.2972 and 0.1262 for organo catalyst loading at pH 6 and 6.5 of organo-silica sols, respectively. On the other hand, the organo-silica matrices in this work showed high surface area 546 m2 g-1 pH 6.5 (0.07 × 10-2 N citric acid) with pore size ~2.9 nm. It is concluded that the xerogels have mesoporous structures, which are effective for further application to separate NaCl in water desalination.
Keywords: mesoporous material; one-step catalyst; organo-silica xerogel; two-step catalyst.