Introduction: Discrepancy between the crown border and prepared tooth margin leads to a microleakage that eases the penetration of microorganisms and causes the dissolution of luting cement consequently. Several factors should be considered to achieve optimal fitness, including tooth preparation taper and type of cementing agent. The study aimed to determine the relation of tooth preparation taper and cement type on the microleakage of zirconia crowns.
Materials and methods: Fifty-six freshly extracted premolars without caries and restorations were selected as the study sample and divided into two groups of different tapering degrees (6 and 12 degrees). Zirconia copings were designed and fabricated by the CAD/CAM system. The samples were divided into four subgroups for cementation, and each subgroup was cemented with a different luting cement (n = 7). After 5000 thermocycles at 5°C-55°C and dye penetration, the specimens were sectioned in the mid-buccolingual direction, and a digital photograph of each section was taken under a stereomicroscope. Data were analyzed by the Kruskal-Wallis and Mann-Whitney tests (α = 0.05).
Results: The results showed significant differences among the four types of luting cement in marginal permeability (PV < 0.001). Regardless of the type of cement, the 12-degree tapering resulted in a lower microleakage (46.4% without microleakage) with statistically significant differences from the 6-degree tapering (PV = 0.042).
Conclusion: Within the limitations of this study, increasing the tapering degree of the prepared tooth for CAD/CAM zirconia copings improved the marginal fit and decreased the microleakage score. In addition, total-etch resin cement indicated the least microleakage.
Copyright © 2021 Behnaz Ebadian et al.