Enhanced water permeability and fouling resistance properties of ultrafiltration membranes incorporated with hydroxyapatite decorated orange-peel-derived activated carbon nanocomposites

Abstract

Hydroxyapatite-decorated activated carbon (HAp/AC) nanocomposite was synthesized and utilized as a nanofiller to fabricate a novel type of polyethersulfone (PES) nanocomposite ultrafiltration (UF) membranes. Activated carbon (AC) derived from orange peel was synthesized by low-temperature pyrolysis at 400 °C. A hydroxyapatite/AC (HAp/AC) nanocomposite was developed by a simple one-pot hydrothermal synthesis method. The UF membrane was fabricated by intercalating HAp/AC fillers into PES casting solution by the non-solvent induced phase separation (NIPS) process. The prepared membranes exhibited a lower water contact angle than the pristine PES membrane. The hybrid membrane with 4 wt% HAp/AC nanocomposite displayed 4.6 times higher pure water flux (~660 L/m² h) than that of the pristine membrane (143 L/m² h). In static adsorption experiments, it was found that the amount of humic acid (HA) and bovine serum albumin (BSA) adsorbed by the HAp/AC-PES hybrid membrane was much lower than that of the original membrane due to the electrostatic repulsive forces between them and the surface of the membrane. Irreversible fouling was reduced from 33 to 6 % for HA and from 46 to 8 % for BSA after HAp/AC was incorporated into the PES matrix. After 7 cycles of water-BSA-water, the HAp/AC-PES hybrid membrane maintained a high pure water flux of 540 L/m² h with an excellent flux recovery ratio (FRR), demonstrating the long-term stability of the membranes. The developed UF membranes outperformed the original PES membranes in terms of permeability, selectivity, and antifouling.

Keywords: Antifouling; High permeable; Hydroxyapatite; Nanocomposites; Orange-peel-derived activated carbon; Ultrafiltration.