Assessing Fracture Toughness and Impact Strength of PMMA Reinforced with Nano-Particles and Fibre as Advanced Denture Base Materials

Abdulaziz Alhotan; Julian Yates; Saleh Zidan; Julfikar Haider; Nikolaos Silikas

doi:10.3390/ma14154127

Assessing Fracture Toughness and Impact Strength of PMMA Reinforced with Nano-Particles and Fibre as Advanced Denture Base Materials

Materials (Basel). 2021 Jul 24;14(15):4127. doi: 10.3390/ma14154127.

Authors

Abdulaziz Alhotan^{1

2}, Julian Yates¹, Saleh Zidan³, Julfikar Haider^{1

4}, Nikolaos Silikas¹

Affiliations

¹ Division of Dentistry, School of Medical Sciences, University of Manchester, Manchester M13 9PL, UK.
² Dental Health Department, College of Applied Medical Sciences, King Saud University, Riyadh 11454, Saudi Arabia.
³ Department of Dental Materials, Faculty of Dentistry, Sebha University, Sebha 18758, Libya.
⁴ Department of Engineering, Manchester Metropolitan University, Manchester M1 5GD, UK.

Abstract

Statement of Problem: Polymethyl methacrylate (PMMA) denture resins commonly fracture as a result of the denture being dropped or when in use due to heavy occlusal forces. Purpose: To investigate the effects of E-glass fibre, ZrO₂ and TiO₂ nanoparticles at different concentrations on the fracture toughness and impact strength of PMMA denture base. Materials and Methods: To evaluate fracture toughness (dimensions: 40 × 8 × 4 mm³; n = 10/group) and impact strength (dimensions: 80 × 10 × 4 mm³; n = 12/group), 286 rectangular tested specimens were prepared and divided into four groups. Group C consisted of the PMMA specimens without any filler (control group), while the specimens in the remaining three groups varied according to the concentration of three filler materials by weight of PMMA resin: 1.5%, 3%, 5%, and 7%. Three-point bending and Charpy impact tests were conducted to measure the fracture toughness and impact strength respectively. Scanning Electron Microscope (SEM) was utilised to examine the fractured surfaces of the specimens after the fracture toughness test. One-way analysis of variance (ANOVA) followed by Tukey post-hoc tests were employed to analyse the results at a p ≤ 0.05 significance level. Results: Fracture toughness of groups with 1.5 and 3 wt.% ZrO₂, 1.5 wt.% TiO₂, and all E-glass fibre concentrations were significantly higher (p < 0.05) than the control group. The samples reinforced with 3 wt.% ZrO₂ exhibited the highest fracture toughness. Those reinforced with a 3 wt.%, 5 wt.%, and 7 wt.% of E-glass fibres had a significantly (p < 0.05) higher impact strength than the specimens in the control group. The heat-cured PMMA modified with either ZrO₂ or TiO₂ nanoparticles did not exhibit a statistically significant difference in impact strength (p > 0.05) in comparison to the control group. Conclusions: 1.5 wt.%, 3 wt.% of ZrO₂; 1.5 wt.% ratios of TiO₂; and 1.5 wt.%, 3 wt.%, 5 wt.%, and 7 wt.% of E-glass fibre can effectively enhance the fracture toughness of PMMA. The inclusion of E-glass fibres does significantly improve impact strength, while ZrO₂ or TiO₂ nanoparticles did not.

Keywords: E-glass fibre; PMMA; TiO2 nanoparticle; ZrO2 nanoparticle; fracture toughness; impact strength.