New types of electromagnetic (EM) wave absorption materials with a light weight, strong absorption ability and wide absorption frequency have been widely explored. Nevertheless, it is still an intractable challenge to design the structure of the materials and rationalize multiple components. In this work, one-dimensional (1D) CoFe2/C@MoS2 composites were prepared via electrospinning technology, high-temperature carbonization and hydrothermal method. SEM and TEM images reveal that the as-prepared CoFe2/C fibers with a 1D structure are well coated with MoS2. The excellent absorption performance of the composites is mainly attributed to the 1D structure and the ideal impedance matching. CoFe2/C@MoS2 composites show strong absorption ability with an optimal reflection loss (RL) of -66.8 dB (13.28 GHz) at a matching thickness of 2.12 mm. Meanwhile, the composite possesses an effective absorption frequency range between 10.70 and 16.02 GHz with a bandwidth of 5.32 GHz. These results indicate that CoFe2/C@MoS2 composites will become promising lightweight and highly efficient MA materials.