A highly permselective nanofiltration membrane was engineered via zwitterionic copolymer assembly regulated interfacial polymerization (IP). The copolymer was molecularly synthesized using single-step free-radical polymerization between 2-methacryloyloxyethyl phosphorylcholine (MPC) and 2-aminoethyl methacrylate hydrochloride (AEMA) (P[MPC-co-AEMA]). The dynamic network of P[MPC-co-AEMA] served as a regulator to precisely control the kinetics of the reaction by decelerating the transport of piperazine toward the water/hexane interface, forming a polyamide (PA) membrane with ultralow thickness of 70 nm, compared to that of the pristine PA (230 nm). Concomitantly, manipulating the phosphate moieties of P[MPC-co-AEMA] integrated into the PA matrix enabled the formation of ridge-shaped nanofilms with loose internal architecture exhibiting enhanced inner-pore interconnectivity. The resultant P[MPC-co-AEMA]-incorporated PA membrane exhibited a high water permeance of 15.7 L·m-2·h-1·bar-1 (more than 3-fold higher than that of the pristine PA [4.4 L·m-2·h-1·bar-1]), high divalent salt rejection of 98.3%, and competitive mono-/divalent ion selectivity of 52.9 among the state-of-the-art desalination membranes.
Keywords: Desalination; Highly permselective property; Interfacial polymerization; Nanofiltration; Polyamide membrane; Zwitterionic copolymer.