In this work, Fe-Ni alloy nanoclusters (Fe-Ni ANCs) anchored on N, S co-doped carbon aerogel (Fe-Ni ANC@NSCA catalysts) are successfully prepared by the optimal pyrolysis of polyaniline (PANI) aerogels derived from the freeze-drying of PANI hydrogel obtained by the polymerization of aniline monomers in the co-presence of tannic acid (TA), Fe3+ , and Ni2+ ions. In addition, the optimal molar ratio of the TA, Fe3+ , and Ni2+ ions for synthesis of Fe-Ni ANC@NSCA catalysts are 1:2:5, which can guarantee the formation of carbon aerogel composed of quasi-2D porous carbon sheets and the formation of high-density Fe-Ni ANCs with an ultrasmall size between 2 to 2.8 nm. These Fe-Ni ANCs consisting of N4 -Fe-O-Ni-N4 moiety are proposed as a new type of active species for the first time, to the best of the authors' knowledge. Thanks to their unique features, the Fe-Ni ANC@NSCA catalysts show excellent performance in oxygen reduction reaction with a half-wave potential (E1/2 ) of 0.891 V and oxygen evolution reaction (260 mV @ 10 mA cm-2 ) in alkaline media as bifunctional catalysts, which are better than the state-of-the-art commercial Pt/C catalysts and RuO2 catalysts. Moreover, Zn-air battery assembled with the Fe-Ni ANC@NSCA catalysts also shows a remarkable performance and exceptionally high stability over 500 h at 5 mA cm-2 .
Keywords: Zn-air battery; carbon aerogel; nanoclusters; oxygen evolution reaction; oxygen reduction reaction.
© 2021 Wiley-VCH GmbH.