Metal-organic frameworks (MOFs) provided a versatile platform for the development of new solid protonic electrolytes but faced great challenges regarding their low chemical stability and poor moisture retention capacity. Herein, we presented the proton-conducting study for zirconium-based MOF-802, revealing that MOF-802 possessed excellent features of extra aqueous and acidic stabilities and room-temperature superprotonic conduction with a proton conductivity of 1.05 × 10-2 S cm-1 at 288 K under 98% relative humidity (RH). Unfortunately, due to the liberation of water molecules from pores/channels, the proton conductivity of MOF-802 dropped significantly at the temperature above 318 K. To solve this issue, for the first time, MOF-802 was hybridized with poly(vinyl alcohol) (PVA) to form MOF-802@PVA hydrogel composites, where the moisture retention capacity of MOF-802 was greatly improved, giving the high room-temperature proton conductivity over 10-3 S cm-1 under ambient humidity. This work paves a new way to improve the moisture retention capacity and proton-conducting performances of porous proton conductors.
Keywords: MOF-802; ambient humidity; hydrogel composites; moisture retention capacity; proton conduction.