TiO2-Doped Ni0.4Cu0.3Zn0.3Fe2O4 Nanoparticles for Enhanced Structural and Magnetic Properties

Asha D Patil; Ram A Pawar; Sunil M Patange; Santosh S Jadhav; Shyam K Gore; Sagar E Shirsath; Sher Singh Meena

doi:10.1021/acsomega.1c01548

TiO₂-Doped Ni_0.4Cu_0.3Zn_0.3Fe₂O₄ Nanoparticles for Enhanced Structural and Magnetic Properties

ACS Omega. 2021 Jul 9;6(28):17931-17940. doi: 10.1021/acsomega.1c01548. eCollection 2021 Jul 20.

Authors

Asha D Patil¹, Ram A Pawar², Sunil M Patange³, Santosh S Jadhav⁴, Shyam K Gore⁴, Sagar E Shirsath⁵, Sher Singh Meena⁶

Affiliations

¹ Deshbhakt Anandrao Balawantrao Naik Art's and Science College, Chikhali, Sangli 415408, Maharashtra, India.
² Department of Physics, Arts, Commerce and Science College, Satral, Ahmednagar 413711, Maharashtra, India.
³ Shri Krishna Mahavidyalaya, Gunjoti, Osmanabad 413606, Maharashtra, India.
⁴ D. S. M's Arts, Commerce and Science College, Jintur 431509, Maharashtra, India.
⁵ University of New South Wales, Sydney NSW 2052, Australia.
⁶ Solid State Physics Division, Bhabha Atomic Research Centre, Mumbai 400085, Maharashtra, India.

Abstract

TiO₂ (0-10 wt %)-doped nanocrystalline Ni_0.4Cu_0.3Zn_0.3Fe₂O₄ (Ni-Cu-Zn) ferrites were synthesized using the sol-gel route of synthesis. The cubic spinel structure of the ferrites having the Fd3m space group was revealed from the analysis of Rietveld refined X-ray diffraction (XRD) data. The secondary phase of TiO₂ with a space group of I41/amd was observed within the ferrites with doping, x > 3 wt %. The values of lattice parameter were enhanced with the addition of TiO₂ up to 5 wt % and reduced further for the highest experimental doping of 10 wt %. Field emission scanning electron microscopy (FESEM) images exhibit the spherical shape of the synthesized particles with some agglomeration, while the compositional purity of prepared ferrite samples was confirmed by energy-dispersive X-ray spectroscopy (EDX) and elemental mapping. The cubic spinel structure of the prepared ferrite sample was confirmed by the Raman and Fourier transform infrared (FTIR) spectra. UV-visible diffuse reflectance spectroscopy was utilized to study the optical properties of the ferrites. The value of band gap energy for the pristine sample was less than those of the doped samples, and there was a decrement in band gap energy values with an increase in TiO₂ doping, which specifies the semiconducting nature of prepared ferrite samples. A magnetic study performed by means of a vibrating sample magnetometer (VSM) demonstrates that the values of saturation magnetization of the ferrites decrease with the addition of TiO₂ content, and all investigated ferrites show the characteristics of soft magnetic materials at room temperature. The Mössbauer study confirms the decrease in the magnetic behavior of the doped ferrites due to the nonmagnetic secondary phase of TiO₂.