In injection molding, the temperature control of the dynamic mold is an excellent method for improving the melt flow length, especially of thin-wall products. In this study, the heating efficiency of a novel heating strategy based on induction heating was estimated. With the use of this heating strategy, a molding cycle time similar to the traditional injection molding process could be maintained. In addition, this strategy makes it easier to carry out the heating step due to the separation of the heating position and the mold structure as well as allowing the ease of magnetic control. The results show that, with an initial mold temperature of 30 °C and a gap (G) between the heating surface and the inductor coil of 5 mm, the magnetic heating process can heat the plate to 290 °C within 5 s. However, with a gap of 15 mm, it took up to 8 s to reach 270 °C. According to the measurement results, when the mold heating time during the molding process increased from 0 to 5 s, the flow length increased significantly from 71.5 to 168.1 mm, and the filling percentage of the thin-wall product also increased from 10.2% to 100%. In general, the application of external induction heating (Ex-IH) during the molding cycle resulted in improved melt flow length with minimal increase in the total cycle time, which remained similar to that of the traditional case.
Keywords: cycle time; dynamic mold temperature control; flow length; induction heating; injection molding; mold heating; thin-wall injection molding.