The hybrid antistatic agent SCNTs/OAA composed of sulfonated carbon nanotubes (SCNTs) and organic antistatic agent (OAA) was treated on the fiber surface to construct the hybrid conductive layer. Among them, SCNTs were synthesized through a simple method, and their chemical structure and morphology were characterized. SCNTs had good dispersibility due to the presence of sulfonic acid groups, which made SCNTs uniformly dispersed on the fiber surface. The SCNTs/OAA-treated fiber was hardly affected by relative humidity, because SCNTs form a continuous and uniform physical conductive network on the fiber surface. When the addition amount of SCNTs/OAA was 0.5~2 wt%, the fiber had excellent antistatic ability. Under the synergistic effect of SCNTs and OAA, the resistivity of SCNTs/OAA-treated fiber was almost not affected by fiber stretching.
Keywords: SCNTs; antistatic agent; conductive layer; fiber.