First experimental evidence of the piezoelectric nature of struvite

Jolanta Prywer; Rafał Kruszyński; Marcin Świątkowski; Andrzej Soszyński; Dariusz Kajewski; Krystian Roleder

doi:10.1038/s41598-021-94410-2

First experimental evidence of the piezoelectric nature of struvite

Sci Rep. 2021 Jul 21;11(1):14860. doi: 10.1038/s41598-021-94410-2.

Authors

Jolanta Prywer¹, Rafał Kruszyński², Marcin Świątkowski², Andrzej Soszyński³, Dariusz Kajewski³, Krystian Roleder³

Affiliations

¹ Institute of Physics, Lodz University of Technology, ul. Wólczańska 219, 90-924, Łódź, Poland. jolanta.prywer@p.lodz.pl.
² Institute of General and Ecological Chemistry, Lodz University of Technology, Żeromskiego 116, 90-924, Łódź, Poland.
³ Institute of Physics, University of Silesia, 75 Pułku Piechoty 1, 41-500, Chorzów, Poland.

Abstract

In this paper, we present the first experimental evidence of the piezoelectric nature of struvite (MgNH₄PO₄·6H₂O). Using a single diffusion gel growth technique, we have grown struvite crystals in the form of plane parallel plates. For struvite crystals of this shape, we measured the piezoelectric coefficients d₃₃ and d₃₂. We have found that at room temperature the value of piezoelectric coefficient d₃₃ is 3.5 pm/V, while that of d₃₂ is 4.7 pm/V. These values are comparable with the values for other minerals. Struvite shows stable piezoelectric properties up to the temperature slightly above 350 K, for the heating rate of 0.4 K/min. For this heating rate, and above this temperature, the thermal decomposition of struvite begins, which, consequently, leads to its transformation into dittmarite with the same non-centrosymmetric symmetry as in case of struvite. The struvite-dittmarite transformation temperature is dependent on the heating rate. The higher the heating rate, the higher the temperature of this transformation. We have also shown that dittmarite, like struvite exhibits piezoelectric properties.