A novel Si-Mn binary modified biochar composite material (SMBC) was prepared after being sintered 450 °C for 2 h. The crystal structure, surface functional groups, surface morphology and element composition, specific surface area and pore structure were characterized by XRD, FTIR, XPS, SEM + EDS and BET etc. The results showed that the surface of SMBC was rough and loose, and the specific surface area increased to 35.4284 m2/g. Si and Mn were uniformly attached to the surface of biochar in the form of SiO2, MnOx, MnSiO3. Batch adsorption experiments showed that SMBC had a higher removal efficiency (139.06 mg/g, above 98%) for Cu(II) when the dosage was 2 g/L and pH = 6. The cycle experiments showed that SMBC had good reusability, and its regeneration efficiency still reached 80.24%. The leaching amount of Mn (0.65 mg/L) was greatly reduced and avoid second-pollution resulted from ion exchange, which was attributed to the existence of Si-O-Mn bonds, and they could help Mn adhere to the surface of biochar more stable. The adsorption process was dominated by single-layer chemical adsorption and mainly occurred in the membrane diffusion stage. Cu(II) mainly formed -COOCu, -OCu, Cu(OH)2, Cu(OH)2CO3, Si-O-Cu, Mn-O-Cu by the mechanisms such as precipitation (4.74%), ion exchange (13.81%), complexation and physical adsorption (total 81.45% of the two mechanisms). Among them, complexation was dominant in the adsorption process.
Keywords: Adsorption; Adsorption mechanism; Biochar; Heavy metals; Si/Mn binary oxide loading.
Copyright © 2021 Elsevier Ltd. All rights reserved.