Yolk-shell silica dioxide spheres @ metal-organic framework immobilized Ni/Mo nanoparticles as an effective catalyst for formic acid dehydrogenation at low temperature

Samikannu Prabu; Kung-Yuh Chiang

doi:10.1016/j.jcis.2021.06.160

Yolk-shell silica dioxide spheres @ metal-organic framework immobilized Ni/Mo nanoparticles as an effective catalyst for formic acid dehydrogenation at low temperature

J Colloid Interface Sci. 2021 Dec 15:604:584-595. doi: 10.1016/j.jcis.2021.06.160. Epub 2021 Jul 2.

Authors

Samikannu Prabu¹, Kung-Yuh Chiang²

Affiliations

¹ Graduate Institute of Environmental Engineering, National Central University, Tao-Yuan City 32001, Taiwan.
² Graduate Institute of Environmental Engineering, National Central University, Tao-Yuan City 32001, Taiwan. Electronic address: kychiang@ncu.edu.tw.

PMID: 34280756
DOI: 10.1016/j.jcis.2021.06.160

Abstract

The novel catalyst with yolk-shell SiO₂ NiMo/SiO₂ spheres immobilized by zeolitic imidazolate framework (ZIF-67) materials has been successfully prepared. The experimental results indicated that the prepared catalyst exhibits superior performance for hydrogen generation from Formic acid (FA) dehydrogenation without any additives at low temperatures. The catalytic performances of the Ni_xMo_1-x/ZIF-67@SiO₂ yolk-shell increased with Ni addition ratio increasing. In this research, Ni_0.8Mo_0.2/ZIF-67@SiO₂ yolk-shell could provide the highest catalytic conversion efficiency. This is due to the uniform dispersion of fine metal nanoparticles (NPs) and synergistic effect between the NiMo NPs and ZIF-67@SiO₂ supporter. The turn over frequency (TOF) value was approximately 13,183 h^-1 at 25 °C through complete FA conversion. H₂ selectivity was also approximately 100% with obvious CO-free hydrogen production at 25 °C. Meanwhile, the prepared NiMo/ZIF-67@SiO₂ yolk-shell catalyst also shows superior catalytic stability with corresponding 99% activity after 10 cycles. In summary, the catalyst preparation and hydrogen generated from FA dehydrogenation obtained from this research could provide the important information for application in catalyst innovation and waste FA recycling and recovery in the future.

Keywords: Bimetallic nanoparticles; Formic acid dehydrogenation; Heterogeneous catalysis; Metal-organic framework; Yolk-shell catalyst.