In compromised bone conditions such as osteoporosis, developments of the implant surface are necessary to secure the stability of implants. This study investigated the effect of the surface porous titanium structure (PS) on the osseointegration of implants in osteoporotic bone. Bilateral ovariectomy (OVX) was performed in 4 female beagle dogs to induce osteoporosis for 32 wk. Success of induction was based on the evaluation of bone mineral density by Hounsfield units (HU) in computed tomography images. Posterior teeth in both mandibles were extracted 1 wk after OVX, and a total of 30 implants (15 implants in each group) were placed after 32 wk of osteoporosis induction. The control group implant underwent resorbable blast media (RBM) surface treatment, whereas the test group underwent RBM surface treatment in the coronal two-thirds and a PS added to the apical 3-mm portion. HU values in the mandibular trabecular bone, lumbar, and femoral head significantly decreased 32 wk after OVX, confirming osteoporotic condition after induction. Resonance frequency analysis and removal torque test showed comparable values between the 2 groups at 4 wk after implant placement. The surface topography of the implant after removal showed hard tissue integration at the PS in the test group. Bone-to-implant contact length was greater in the apical portion of the test group, although statistical significance was not found between the groups. Interthread bone area in the apical portion of the test group showed a significant increase compared to the control group (control: 0.059 ± 0.041 mm2, test: 0.121 ± 0.060 mm2, P = 0.028) with the histological feature of bone ingrowth at the PS. The findings of the study demonstrated that the surface PS could improve osteoconductivity in the osteoporotic trabecular bone by bone ingrowth at the pore space, thereby enhancing the osseointegration and stability of the implants.
Keywords: animals; bone-implant interface; dental implant; osseointegration; ovariectomy; porosity.