Laser powder bed fusion (LPBF) of Cu-0.5Cr was carried out using recycled powder taken out from the LPBF machine after previous printing. Various volumetric defects characterized the powder wherein particle size distribution was the same as virgin powder. Using recycled powder resulted in extra spherical pore formation after the LPBF process. Despite that, a relative density of 99.2% was achieved by LPBF parameters optimization. Solidified microstructure with a small volume of defects consisted of an oversaturated dendritic Cu matrix and nano-sized Cr precipitations providing strengthening mechanism occurrence. The possibility of a satisfactory level of mechanical properties with σ0.2 = 136.8 MPa, UTS = 187.4 MPa, along with 15.5% of elongation achieving, was shown.
Keywords: bronze; chromium bronze; laser powder bed fusion; mechanical properties; selective laser melting.