Purpose: The purpose of this study was to examine morphological changes in the superstructure of implants in relation to the degree of attrition of the implant superstructure and its antagonists.
Methods: Thirty-three patients participated. The implant superstructures of the first molar and its antagonists were scanned with an intraoral scanner every 3 months. The amount of attrition was calculated in relation to the various materials used for the superstructure, and differences were analyzed statistically (P < 0.05).
Results: Attrition of the implant superstructure was 110 ± 30 µm for monolithic zirconia and 105 ± 27 µm for resin-veneered metal after 12 months. No statistically significant difference was found between the two groups. In contrast, attrition of the antagonists was 75 ± 25 µm for zirconia and 105 ± 20 µm for resin-veneered metal after 12 months. A statistically significant difference in the attrition levels between the two groups was observed after 9 and 12 months.
Conclusion: During the 12-month observation period, there was no difference in superstructure attrition between zirconia and resin-veneered metal. Attrition of the antagonists was higher for hybrid composite resin-veneered metal than for zirconia, suggesting that surface roughness affected the degree of attrition.
Keywords: attrition; dental implant; implant superstructure; intraoral scanner; zirconia.