Porous ceramic membrane supports with high mechanical strength and permeation are required for highly permeable ceramic membranes. The water permeation of a ceramic membrane support is largely dependent on its level of open porosity, which can be however generally detrimental to the mechanical strength. In this work, low-cost kaolin nanoflakes were rationally composited with coarse alumina particles, and multichannel flat-sheet ceramic supports were successfully fabricated by extrusion and subsequent partial sintering. The macroscopic properties, microstructure characteristics, permeability, and mechanical strength of the ceramic membrane supports were systematically established and comprehensively studied. The incorporation of kaolin nanoflakes effectively reduced the sintering temperature to about 1200 °C. An interesting evolution of the pore structure was evidenced with the increase in sintering temperature. Interestingly, the porous ceramic supports prepared at 1400 °C with a nominal pore size of 1.47 μm showed the highest water permeability of 9911.9 ± 357.5 LMHB, and at the same time the flexural strength reached 109.6 ± 4.6 MPa. The much improved permeability was attributed to the unique multilevel pore structures, and the enhanced flexural strength mainly originated from the strongly interfacial bonding, as evidenced by the trans-granular fracture behavior. Also, the ceramic membrane supports exhibited excellent chemical resistance and good removal efficiency for oily wastewater. This work highlights the significant role of interfacial engineering in simultaneously improving the water permeation and mechanical strength, thereby overcoming their trade-off in porous ceramic membrane supports.
Keywords: ceramic membranes; interfacial engineering; mechanical strength; oily wastewater treatment; water permeation.