Objectives: To investigate the effect of different pre-treatments on the long-term bond strength of fiberglass posts luted either with dual-curing self-etch adhesives and core build-up composites or with a self-adhesive resin (SAR) cement.
Materials and methods: In total, 180 human root-filled teeth received post-space preparations and three different dentin pre-treatments (PTs): PT1, ethanol (99%); PT2, ethanol-tertiary-butanol-water-solution (AH Plus Cleaner, Dentsply Sirona; York, USA); and PT3, distilled water (control). Five luting systems were used: FU, Futurabond U (Voco; Cuxhaven, Germany); CL, Clearfil DC Bond (Kuraray Noritake; Okayama, Japan); GR, Gradia Core SE Bond (GC Europe NV; Leuven, Belgium); LU, LuxaBond Universal (DMG; Hamburg, Germany); and RX, RelyX Unicem 2 (3M; Minnesota, USA). Roots were cut into six slices (1 mm thick). From each root canal region, three slices were submitted to immediate and three to post-storage push-out testing. The latter were subjected to thermocycling (5-55°C, 6.000 cycles) and stored for six months in saline solution (0.9%, 37°C). Data were analysed using repeated measures ANOVA and chi-square tests (MV±SD).
Results: Bond strength was significantly affected by material (p<0.0005), pre-treatment (p=0.016), and storage (p<0.0005; repeated-measures ANOVA). LU (18.8±8.1MPa) revealed significantly higher bond strength than RX (16.08±6.4MPa), GR (15.1±4.6MPa), CL (13.95±5.2MPa), and FU (13.7±6.3MPa). PT1 (16.5±6.9MPa) revealed significantly higher bond strength than PT3 (14.5±5.7MPa).
Conclusions: A universal adhesive in self-etch mode combined with a core build-up material revealed higher bond strength than a SAR cement, both interacted positively with Ethanol pre-treatment.
Clinical relevance statement: Ethanol (99%) rinsing can be recommended as part of post and core pre-treatment for the investigated luting systems.
Keywords: Ethanol pre-treatment; Push-out bond strength; Root canal dentin; Self-etch adhesives; Thermocycling.