Carbon fiber/microlattice 3D hybrid architecture as multi-scale scaffold for tissue engineering

Abstract

Multiscale 3D carbon architectures are of particular interest in tissue engineering applications, as these structures may allow for three-dimensional cell colonization essential for tissue growth. In this work, carbon fiber/microlattice hybrid architectures are introduced as innovative multi-scale scaffolds for tissue engineering. The microlattice provides the design freedom and structural integrity, whereas the fibrous component creates a cellular microenvironment for cell colonization. The hybrid structures are fabricated by carbonization of stereolithographically 3D printed epoxy microlattice architectures which are pre-filled with cotton fibers within the empty space of the architectures. The cotton filling result in less shrinkage of the architecture during carbonization, as the tight confinement of the fibrous material prevents the free-shrinkage of the microlattices. The hybrid architecture exhibits a compressive strength of 156.9±25.6 kPa, which is significantly higher than an empty carbon microlattice architecture. Furthermore, the hybrid architecture exhibits a flexible behavior up to 30% compressive strain, which is also promising towards soft-tissue regeneration. Osteoblast-like murine MC3T3-E1 cells are cultured within the 3D hybrid structures. Results show that the cells are able to not only proliferate on the carbon microlattice elements as well as along the carbon fibers, but also make connections with each other across the inner pores created by the fibers, leading to a three-dimensional cell colonization. These carbon fiber/microlattice hybrid structures are promising for future fabrication of functionally graded scaffolds for tissue repair applications.

Keywords: 3D carbon structure; Additive manufacturing; Carbon fibers; Carbon microlattices; Multi-scale structure; Tissue engineering.