CdTe QDs has been demonstrated in many studies to possess good outstanding optical and photo-physical properties. However, it has been established from literature that the toxic Cd2+ that tends to leak out into nearby solutions can be protected by less toxic ZnS or ZnSe shells leading to the synthesis of core-shells and multi-core-shells. Hence, this has allowed the synthesis of CdTe multi-core-shells to have gained much interest. The preparation of most CdTe multi-core-shells reported from various studies usually has a longer reaction time (6-24 h) in reaching their highest emission maxima. The synthesis of CdTe multi-core-shells in this study only took 35 min to obtain a highest emission maximum compared to what has been reported from the literature. CdTe multi-core-shells were synthesized by injecting 7, 14, and 21 mL each of Zn complex solution and Se ions into the reacting mixture containing CdTe core-shells (3 h) at 5 min intervals over a 35 min reaction time. The emission maxima of the MPA-TGA-CdTe multi-core-shells at 21 mL injection was recorded around 625 nm. Therefore, we are reporting the rapid synthesis of five different thiol co-capped CdTe/CdSe/ZnSe multi-core-shell QDs with the highest emission maxima obtained at 35 min reaction time.
Keywords: CdTe multi-core-shell; rapid synthesis; thiol dual-capped.