A new route has been developed to design plasmonic pollen grain-like nanostructures (PGNSs) as surface-enhanced Raman scattering (SERS)-active substrate. The nanostructures consisting of silver (Ag) and gold (Au) nanoparticles along with zinc oxide (ZnO) nanoclusters as spacers were found highly SERS-active. The morphology of PGNSs and those obtained in the intermediate stage along with each elemental evolution has been investigated by a high-resolution field emission scanning electron microscopy. The optical band gaps and crystal structure have been identified by UV-vis absorption and X-ray powder diffraction (XRD) measurements, respectively. For PGNSs specimen, three distinct absorption bands related to constituent elements Ag, Au, and ZnO were observed, whereas XRD peaks confirmed the existence of Ag, Au, and ZnO within the composition of PGNSs. SERS-activity of PGNSs was confirmed using Rhodamine 6G (R6G) as Raman-active dyes. Air-cooled solid-state laser kits of 532 nm were used as excitation sources in SERS measurements. SERS enhancement factor was estimated for PGNSs specimen and was found as high as 3.5×106 . Finite difference time domain analysis was carried out to correlate the electromagnetic (EM) near-field distributions with the experiment results achieved under this investigation. EM near-field distributions at different planes were extracted for s-, p- and 45° of incident polarizations. EM near-field distributions for such nanostructures as well as current density distributions under different circumstances were demonstrated and plausible scenarios were elucidated given SERS enhancements. Such generic fabrication route as well as correlated investigation is not only indispensable to realize the potential of SERS applications but also unveil the underneath plasmonic characteristics of complex SERS-active nanostructures.
Keywords: Nanostructures; electromagnetic near-field distribution; finite difference time domain; plasmonics; surface-enhanced Raman scattering.
© 2021 Wiley-VCH GmbH.