Advanced materials and processes are required to separate halides and fission products from complex salt waste streams associated with the chemical reprocessing of used nuclear fuels and molten salt reactor technologies for immobilization into chemically durable waste forms. In this work, we explore an innovative concept using metal halide perovskites as advanced host phases to incorporate Cs and Cl with very high waste loadings. Wet chemistry-synthesized Cs2SnCl6 powders from CsCl salt solutions are successfully encapsulated into a silica matrix to form a composite using low-temperature spark plasma sintering with tunable Cs and Cl loadings up to 31 and 26 wt %, respectively. Chemical durability testing of the composite waste forms by semi-dynamic leaching experiments demonstrates that an incongruent leaching mechanism dominates the release of Cs and Cl. The metal halide perovskite-silica composite waste forms display exceptional chemical durability with the long-term release rates of Cs and Cl comparable to or outperforming the state-of-the-art waste form materials but with significantly higher waste loadings. The scalable synthesis of the metal halide perovskite from wet chemistry processes opens up new opportunities in designing advanced waste forms for salt wastes with very high waste loadings and exceptional chemical durability for the sustainable development of advanced fuel cycles and next-generation reactor technologies.
Keywords: advanced waste forms; chemical durability; high chloride salt waste; metal halide perovskites.