The properties and microstructure evolution of quaternary Cu-Ni-Co-Si alloys with different Ni/Co mass ratios were investigated. The microstructure and morphological characteristics of the precipitates were analyzed by using electron backscatter diffraction (EBSD), transmission electron microscopy (TEM) and high-resolution transmission electron microscopy (HRTEM). The mechanical properties and conductivity of the alloys were significantly improved after the addition of Co. The grains presented an obvious growth trend with an increase in Ni/Co mass ratios, and the appropriate Co accelerated the recrystallization process. The δ-(Ni, Co)2Si phases of the Cu-Ni-Co-Si alloys and δ-Ni2Si phases of the Cu-Ni-Si alloys shared the same crystal structure and orientation relationships with the matrix, which had two variant forms: δ1 and δ2 phases. The precipitates preferential grew along with the direction of the lowest energy and eventually exhibited two different morphologies. Compared with that of the Cu-Ni-Si alloy, the volume fraction of precipitates in the alloys with Co was significantly improved, accompanied by an increase in the precipitated phase size. The addition of Co promoted the precipitation of the precipitated phase and further purified the matrix. A theoretical calculation was conducted for different strengthening mechanisms, and precipitation strengthening was the key reinforcement mechanism. Moreover, the kinetic equations of both alloys were obtained and coincided well with the experimental results.
Keywords: Cu-Ni-Si-based alloys; Ni/Co mass ratio; kinetic equation; microstructure; strengthening mechanism.