The use of waste streams for the production of sustainable cement-based materials cannot be overemphasized. This study investigates the feasibility of reusing waste steel slag (WSS) and waste clay brick (WCB) as a replacement for natural sand (NS) in mortar. Numerous studies have reported mainly the compressive strength of concrete/mortar, while limited research is available that focuses on the tensile and flexural strength of mortar, and especially the performance at elevated temperature. Hence, this study investigates the tensile and flexural strength of mortar with three different replacement percentages (0, 50 and 100% by volume of NS) of NS by WSS and WCB at normal temperature (without thermal treatment) and after exposure to elevated temperatures (250, 400 and 600 °C). At ambient condition, both tensile and flexural strength were enhanced as the WSS content increased (76 and 68%, respectively, at 100% WSS). In comparison, the strength increased at 50% WCB (25 and 37%, accordingly) and decreased at 100% WCB (23 and 20%, respectively) compared to 100% NS. At elevated temperatures, both the tensile and flexural strength of mortar mixes decreased significantly at 600 °C.
Keywords: elevated temperatures; mortar; tensile and flexural strength; waste clay brick; waste steel slag.