Exploring electrocatalysts with satisfactory activity and durability has remained a long-lasting target for electrolyzing water, which is particularly significant for sustainable hydrogen fuel production. Here, we report a quaternary B/P-codoped transition metal Co-Mo hybrid as an efficient alternative catalyst for overall water splitting. The Co-Mo-B-P/CF dual nanowafers were deposited on a copper foam by double-pulse electrodeposition, which is favorable for achieving a nanocrystalline structure. The Co-Mo-B-P/CF catalyst shows a high catalytic activity along with good long-term stability in 1.0 M KOH solutions for both the hydrogen and oxygen evolution reactions, requiring 48 and 275 mV to reach 10 mA cm-2, respectively. The synergetic effect between Co-Mo and doped B and P elements is mainly attributed to the excellent bifunctional catalysis performance, while the dual-nanowafer structure endows Co-Mo-B-P with numerous catalytical active sites enhancing the utilization efficiency of atoms. Moreover, the catalytic capability of Co-Mo-B-P/CF as a bifunctional electrocatalyst for the overall water splitting is proved, with the current density of 10 mA cm-2 accomplished at 1.59 V. After the stability test for overall water splitting at 1.59 V for 24 h, the activity almost remains unchanged. The features of excellent electrocatalytic activity, simple preparation, and inexpensive raw materials for Co-Mo-B-P/CF as a bifunctional catalyst hold great potentials for overall water splitting.
Keywords: Co-Mo-B-P/CF; dual nanowafers; hydrogen evolution; overall water splitting; oxygen evolution.