Laser assisted synthesis of silicon nanowires (SiNWs) was successfully achieved through the use of gold and nickel as catalysts. The diameter of the resulting SiNWs was found to be dependent on that of the catalyst in the case of gold catalyst. The gold catalysed silicon nanowires were unevenly curved and branched owing to the high kinetic energy possessed by gold nanoparticles (AuNPs) at relatively high processing temperature. The use of nickel as catalyst resulted in the formation of several SiNWs on a single nickel catalyst crystallite due to interconnection of the nickel metal crystallites at processing temperature. The morphology of SiNWs catalysed by both nickel and gold was controlled by optimising the laser energy during ablation.