The article presents the results of studies on the influence of Mg on the formation of the periodic layered structure of the Zn-AlMg coatings. These coatings were produced by the double batch hot dip method in a Zn bath and then in a Zn-Al(Mg) bath with a content of 15, 23, 31 wt.% Al and 3, 6 wt.% Mg. The microstructure of the coatings (OM, SEM) was revealed and the phase composition (XRD) obtained in two-component Zn-Al baths and Zn-AlMg baths were determined. The periodic layered structure was found to consist of alternating FeAl3 phase layers and a bath alloy (Zn + Al + Mg). Moreover, it was observed that the addition of 3 wt.% Mg reduces the thickness of the coating in baths containing 23 and 31 wt.% Al. However, the addition of 6 wt.% Mg causes complete disappearance of periodic layered structure in a bath with 23 wt.% Al. In a bath with a content of 31 wt.% Al the addition of 6 wt.% Mg creates a compact layer consisting of the FeAl3 phase containing the precipitation of the MgZn2 phase and Fe2Al5 phase. Such a structure of the coating transition layer limits the growth of the periodic layered structure in the coating.
Keywords: Zn-AlMg bath; hot dip galvanizing; periodic layered structure.