Formation of reactive oxygen species (ROS) via H2O2 activation is of vital importance in catalytic environmental chemistry, especially in degradation of organic pollutants. A new mixed niobium-cerium oxide (NbCeOx) was tailored for this purpose. A thorough structural and chemical characterization of NbCeOx along with CeO2 and Nb2O5 reference materials was carried out using TEM/STEM/EDS, SEM, XRD, XPS, EPR, UV-vis and N2 physisorption. The ability of the catalysts to activate H2O2 towards ROS formation was assessed on the basis of EPR and Raman measurements. Catalytic activity of the oxides was evaluated in degradation of methylene blue (MB) as a model pollutant. Very high activity of NbCeOx was attributed to the mixed redox-acidic nature of its surface, which originated from the synergy between Nb and Ce species. These two properties (redox activity and acidity) ensured convenient conditions for efficient activation of H2O2 and degradation of MB. The activity of NbCeOx in MB degradation was found 3 times higher than that of the commercial Nb2O5 CBMM catalyst and 240 times higher than that of CeO2. The mechanism of the degradation reaction was found to be an adsorption-triggered process initiated by hydroxyl radicals, generated on the surface via the transformation of O2-•/O22-.
Keywords: Fenton-like processes; Methylene blue degradation; Mixed oxides; Reactive oxygen species; Wet peroxide oxidation.
Copyright © 2021 The Authors. Published by Elsevier B.V. All rights reserved.