This work intends to synthesis newer guar gum indole acetate ester and design film scaffolds based on protein-polysaccharide interactions for tissue engineering applications. Guar gum indole acetate(GGIA) was synthesized for the first time from guar gum in presence of aprotic solvent activated hofmeister ions. The newer biopolymer was fully characterized in FT-IR,13C NMR, XRD and TGA analysis. High DS (Degree of Substitution, DS = 0.61) GGIA was cross-linked with hydrolyzed keratin, extracted from chicken feather wastes. Films were synthesized from different biopolymer ratios and the surface chemistry appeared interesting. Physicochemical properties for GGIA-keratin association were notable. Fully bio-based films were non-cytotoxic and exhibited excellent biocompatibility for human dermal fibroblast cell cultivations. The film scaffold showed 63% porosity and the recorded tensile strength at break was 6.4 MPa. Furthermore, the standardised film exerted superior antimicrobial activity against both the Gram-positive and Gram-negative bacteria. MICs were recorded at 130 μg/mL and 212 μg/mL for E. coli and S. aureus respectively. In summary, GGIA-keratin film scaffolds represented promising platforms for skin tissue engineering applications.
Keywords: Chicken feather keratin; Guar gum; Guar gum indole acetate; Protein-polysaccharide interactions; Tissue engineering.
Copyright © 2021 Elsevier B.V. All rights reserved.