Prospects for Electrical Performance Tuning in Ca3Co4O9 Materials by Metallic Fe and Ni Particles Additions

Gabriel Constantinescu; Sergey M Mikhalev; Aleksey D Lisenkov; Daniela V Lopes; Artur R Sarabando; Marta C Ferro; Tiago F da Silva; Sergii A Sergiienko; Andrei V Kovalevsky

doi:10.3390/ma14040980

Prospects for Electrical Performance Tuning in Ca₃Co₄O₉ Materials by Metallic Fe and Ni Particles Additions

Materials (Basel). 2021 Feb 19;14(4):980. doi: 10.3390/ma14040980.

Authors

Gabriel Constantinescu¹, Sergey M Mikhalev², Aleksey D Lisenkov¹, Daniela V Lopes¹, Artur R Sarabando¹, Marta C Ferro¹, Tiago F da Silva¹, Sergii A Sergiienko¹, Andrei V Kovalevsky¹

Affiliations

¹ Department of Materials and Ceramics Engineering, CICECO-Aveiro Institute of Materials, University of Aveiro, 3810-193 Aveiro, Portugal.
² TEMA-NRD, Mechanical Engineering Department, Aveiro Institute of Nanotechnology (AIN), University of Aveiro, 3810-193 Aveiro, Portugal.

Abstract

This work further explores the possibilities for designing the high-temperature electrical performance of the thermoelectric Ca₃Co₄O₉ phase, by a composite approach involving separate metallic iron and nickel particles additions, and by employing two different sintering schemes, capable to promote the controlled interactions between the components, encouraged by our recent promising results obtained for similar cobalt additions. Iron and nickel were chosen because of their similarities with cobalt. The maximum power factor value of around 200 μWm^-1K^-2 at 925 K was achieved for the composite with the nominal nickel content of 3% vol., processed via the two-step sintering cycle, which provides the highest densification from this work. The effectiveness of the proposed approach was shown to be strongly dependent on the processing conditions and added amounts of metallic particles. Although the conventional one-step approach results in Fe- and Ni-containing composites with the major content of the thermoelectric Ca₃Co₄O₉ phase, their electrical performance was found to be significantly lower than for the Co-containing analogue, due to the presence of less-conducting phases and excessive porosity. In contrast, the relatively high performance of the composite with a nominal nickel content of 3% vol. processed via a two-step approach is related to the specific microstructural features from this sample, including minimal porosity and the presence of the Ca₂Co₂O₅ phase, which partially compensate the complete decomposition of the Ca₃Co₄O₉ matrix. The obtained results demonstrate different pathways to tailor the phase composition of Ca₃Co₄O₉-based materials, with a corresponding impact on the thermoelectric performance, and highlight the necessity of more controllable approaches for the phase composition tuning, including lower amounts and different morphologies of the dispersed metallic phases.

Keywords: composite approach; controlled interactions; electrical performance; thermoelectric cobaltites; transition metals additions.

Abstract

Grants and funding