Development of thick paste-like inks based on superconcentrated gelatin/alginate for 3D printing of scaffolds with shape fidelity and stability

Abstract

Shape fidelity and integrity are serious challenges in the 3D printing of hydrogel precursors, as they can influence the overall performance of 3D scaffolds. This work reports the development of superconcentrated inks based on sodium alginate and fish gelatin as an appealing strategy to satisfy such challenges and dictate the quality of the printed scaffolds, without using crosslinking strategies during 3D printing. SEM micrographs and micro-CT images indicate the homogeneous distribution of the polysaccharide in the gelatin-based matrix, suggesting its potential to act as a reinforcing additive. The high concentration of gelatin aqueous solution (50 wt%) and substantial incorporation of alginate have facilitated the highly accurate printability and influence the in vitro stability and mechanical properties of the printed scaffolds. An improvement of the stiffness is dictated by the increase of alginate concentration from 20 wt% to 25 wt%, and an increase of Young modulus with about 46% is reached, confirming the reinforcing effect of polysaccharide. This study highlights the potential of paste-type inks to provide high resolution 3D printed structures with appealing structural and dimensional stability, in vitro degradability and mechanical properties for biomedical applications.

Keywords: 3D printing; Additive manufacturing; Alginate; Gelatin; Hydrogel scaffolds; Thick paste-like ink.