On the synergistic effect of sulfonic functionalization and acidic adhesive conditioning to enhance the adhesion of PEEK to resin-matrix composites

Abstract

Objective: The objective of this study was to evaluate the combined effect of the sulfuric acid etching and an acidic adhesive conditioning on the shear bond strength of PEEK to a resin-matrix composite.

Materials and methods: Forty PEEK specimens were assigned randomly to 4 groups for H₂SO₄ etching followed by universal adhesive (pH at 2.5) conditioning for 0, 1, 3, and 5 min. Thirty PEEK specimens were divided into 3 groups for only acidic adhesive conditioning for 0, 1, 3, and 5 min. After the light-curing of the adhesive, a nanohybrid resin composite was applied onto the surfaces and then light-cured following the manufacturer`s guidelines. All specimens were stored in distilled water at 37 °C for 24 h mechanical testing. Shear bond strength tests were performed using a universal testing machine. Surfaces were analyzed by SEM, light interferometry, FTIR, and liquid contact angle measurement. Statistical analysis was performed by one-way ANOVA and Tukey's post hoc tests (p < 0.05).

Results: No adhesion was achieved between untreated PEEK a resin-matrix composite, regardless of the adhesive conditioning time points. Shear bond strength of H₂SO₄-etched PEEK to resin-matrix composite increased with time (0 mmin. 4.95 ± 2.86 MPa < 1 min: 9.35 ± 2.26 MPa < 3 min: 17.84 ± 2.82 MPa < 5 min: 21.43 ± 5.00 MPa). SEM images revealed a significant modification of PEEK surface topography after the H₂SO₄ etching.

Significance: The acidic adhesive was unable to modify the untreated PEEK surface to establish an effective adhesion although a synergistic effect was noticed when the universal (acidic) adhesive was applied over a H₂SO₄-etched PEEK surface, thus improving the PEEK to resin-matrix composite adhesion.

Keywords: Adhesion; Etching; PEEK; Resin composite; Shear bond strength; Universal adhesive.