Carbon fiber dispersion has a substantial influence on the properties of amorphous calcium silicate hydrate-based contact-hardening composites. In this study, a mixture of carbon fiber and calcium silicate hydrate powder was compressed into solid composites at 40 MPa for one minute. The mechanical properties and electrical resistivity of the solid materials were measured, and the dispersion of carbon fibers was quantitatively evaluated by digital image processing technology. The Taipalu model was used to build the correlation between the electrical resistivity of the composites and the carbon fiber dispersion. The results of the electrical resistivity showed that the down threshold of carbon fiber content in the contact-hardening composites was 1.0 wt.% and the electrical resistivity was 30,000 Ω·cm. As the fiber content increased to 2.0 wt.%, the electrical resistivity dropped to 2550 Ω·cm, which was attributed to the increase in fiber dispersion uniformity in the solid composites, and the value of the fiber distribution coefficient reached a maximum value of 0.743. A subsequent decrease in the uniformity of the fiber dispersion was observed at a high fiber content. In addition, the carbon fiber content showed a slight influence on the fiber orientation in the contact-hardening composites.
Keywords: Taipalu model; carbon fiber dispersion; contact-hardening composites; digital image processing technology; electrical conductivity.