Component ratios and kinetics are key to understanding and optimising novel formulations. This warrants investigation of valid methods. Attenuated Total Reflectance Fourier Transform Infra-Red (ATR)-FTIR spectra of separate primers/adhesives were modelled using summed spectra of solvents (water, ethanol), methacrylate monomers (HEMA (hydroxyethyl methacrylate), Bis-GMA (bisphenol A glycidyl methacrylate), and 10-MDP (10-methacryloyloxydecyl dihydrogen phosphate)), and fillers, multiplied by varying fractions. Filler loads were obtained following their separation from the adhesives, by analysing three repetitions (n = 3). Spectral changes during light exposure at 37 °C (20 s, LED 1100-1330 mW/cm2) were used to determine polymerisation kinetics (n = 3). Independent samples T-test was used for statistical analysis (significance level of 5%). FTIR modelling suggested a primer solvent percentage of OBFL (Optibond FL) (30%) was half that of CFSE (Clearfil SE 2) (60%). OBFL included ethanol and water, while CFSE included only water. Monomer peaks were largely those of HEMA with lower levels of phosphate monomers. OBFL/CFSE adhesive model spectra suggested that both contained equal volumes of Bis-GMA/HEMA, with CFSE having 10-MDP. Filler levels and spectra from OBFL (48 wt.%) and CFSE (5 wt.%) were different. Both systems reached a 50% conversion rate within seconds of light exposure. The final conversion for OBFL (74 ± 1%) was lower compared to CFSE (79 ± 2%) (p < 0.05). ATR-FTIR is a useful method to investigate relative levels of main components in bonding systems and their polymerisation kinetics. Such information is valuable to understanding such behaviour.
Keywords: FTIR; dental adhesives; infra-red spectroscopy; photopolymerisation; prediction model.