Flexible ionogels with good mechanical properties were obtained in situ by thiol-ene photopolymerization of trimethylolpropane tris(3-mercaptopropionate) (TMPTP) and 1,3,5-triallyl-1,3,5-triazine-2,4,6(1H,3H,5H)-trione (TATT) (with C=C: SH ratio 1:1) in four imidazolium ionic liquids (1-ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide-EMImNTf2, 1-ethyl-3-methylimidazolium trifluoromethanesulfonate-EMImOTf, 1-butyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide-BMImNTf2, and 1-butyl-3-methylimidazolium trifluoromethanesulfonate-BMImOTf) used in the range 50 to 70 wt.%. The mechanical and electrochemical properties of obtained ionogels were examined. Ionogels with ionic liquids (ILs) with NTf2- anion are more puncture resistant than with OTf⁻ anion. Moreover, ionogels with the NTF2- anion have better electrochemical properties than those with the OTf⁻ anion. Although it should be noted that ionogels with the EMIm+ cation have a higher conductivity than the BMIm+. This is connected with intermolecular interactions between polymer matrix and IL related to the polarity of IL described by the Kamlet-Taft parameters. These parameters influence the morphology of the polymer matrix (as shown by the SEM micrograph), which is formed by interconnected polymer spheres.
Keywords: electrochemical capacitor; gel polymer electrolytes; ionogels; mechanical properties; thiol-ene photopolymerization.