In this study, cement minerals, aluminates, and alkali-free accelerators incorporated with steel fiber were used to scrutinize the influence of accelerating agents on the long-term performance of tunneling shotcrete. Performance tests were identified based on the core compressive strength of mix shotcrete specimens with different types of accelerating agents throughout timeframes of 1, 3, 6, and 12 months. Here, 37 kg of steel fiber was incorporated into the cement mineral and aluminate mixes, and 40 kg of steel fiber was incorporated in an alkali-free mix for the shotcrete mix design. The KSF 2784 and ASTM 214 standards were followed for specimen fabrication and core cutting. For all specimens, shotcrete test panels of 250 × 600 × 500 mm were manufactured for core compressive strength tests conducted using 100, 75 and 55 mm diameter cylindrical molds and a length-to-diameter ratio of 2. The 1-month compressive strength of all test variables satisfied the Korea Expressway Co. standard of 21 MPa. The core compressive strength of the shotcrete specimens showed a tendency to increase with age, but a strength reduction occurred in 6 months and increased again at 12 months. Moreover, the impact of the diameter changes in the shotcrete core specimens was analyzed based on the mixing. For 12 months, a large increase in the core compressive strength occurred, particularly in the alkali-free specimens. The comparison also focused on the relative strength compared with a cast concrete mold and shotcrete core specimens. It is necessary to use alkali-free accelerators considering the long-term performance of tunnels and worker safety.
Keywords: accelerators types; alkali-free accelerators; aluminate accelerator; cement mineral accelerator; core compressive strength; long term performance; steel fiber shotcrete; tunnel site.