Ceramic materials based on naturally occurring clays are a low cost and environmentally friendly alternative to commercial polymer-based membranes in bioelectrochemical systems. In this work, ceramic membranes containing different amounts of iron oxide (1.06, 2.76 and 5.75 vol.%) and sintered at different temperatures (1100, 1200 and 1300 °C) have been elaborated and tested as separators in urine-fed microbial fuel cells (MFCs). The results reveal that the presence of iron oxide in the ceramic membrane composition increases the structural porosity and reduces the pore size for the three temperatures investigated. On the other hand, it was also observed that the iron content mitigates the negative effect of the high sintering temperature on the power performance of the MFCs. In the case of the ceramic membranes sintered at 1300 °C, power output improved ca. 10-fold when the iron oxide content in the membrane increased from 1.06 up to 5.75 vol.% (30.9 and 286.6 µW, respectively). Amongst the different combinations of iron phase content and sintering temperatures, the maximum power output was obtained by MFCs working with separators containing 5.75 vol. % of iron oxide and sintered at 1100 °C (1.045 mW). Finally, the system was stable for 65 days, which supports the long-term functionality of the different materials assessed.
Keywords: Bioenergy; Ceramic membranes; Iron oxide content; Microbial fuel cells; Urine.
© 2020 The Authors. Published by Elsevier Ltd.