In this research a bench scale rotating biological contactor (RBC) was designed and constructed to produce BC. The effects of variables including rotation speed of the disk, distance between disks, disk type and external aeration on BC productivity were investigated. Results showed that the highest weight of BC produced on the surface of integrated polyethylene discs which rotated at 13 rpm. It was also found that the highest amount of BC was obtained when the space between two adjacent discs was adjusted to 1 cm and the disk number was 16. An aquarium pump was used to investigate the impact of aeration on RBC made of 12 integrated polyethylene discs and operated at optimal rotation speed of 13 rpm. Disk spacing distance was adjusted to 1.5 cm to consider the possible increasing of the thickness of BC film by aeration. Wet weight and dry weight of BC resulted from aerated fermentation increased more than 64 and 47%, respectively as compared to non-aerated RBC. In comparison with static culture, wet weight and dry weight of BC produced in aerated RBC fermentation increased more than 90.7 and 71%, respectively. Nanoscale structure of produced bacterial cellulose was confirmed by SEM analysis.
Keywords: Acetobacter xylinium; Bacterial nano-cellulose; Productivity; Rotating biological contactor (RBC).