A 3YSZ (3 mol% yttria-stabilized zirconia) ceramic green body with 50 vol% of ceramic content was 3D-printed by supportless stereolithography under optimal drying, debinding, and sintering conditions in order to achieve high strength and density. The viscosity and flowability of the ceramic nanocomposite resins were optimized by adjusting the amounts of non-reactive diluents. The ceramic 3D-printed objects have a high polymer content compared to ceramics samples manufactured by conventional manufacturing processes, and the attraction between layers is weak because of the layer-by-layer additive method. This causes problems such as layer separation and cracking due to internal stress generated when materials such as solvents and polymers are separated from the objects during the drying and debinding processes; therefore, the drying and debinding conditions of 3YSZ ceramic 3D-printed objects were optimized based on thermogravimetry-differential thermal analysis. The sintering conditions at various temperatures and times were analyzed using X-ray diffraction, SEM, and flexural strength analysis, and the body of the 3YSZ ceramic 3D-printed object that sintered at 1450 °C for 150 min had a relative density of 99.95% and flexural strength of 1008.5 MPa. This study widens the possibility of manufacturing ceramic 3D-printed objects with complex shapes, remarkable strength, and unique functionality, enabling their application in various industrial fields.
Keywords: 3D printing; 3YSZ; flexural strength; relative density; sintering.