Terahertz time-domain spectroscopy (THz-TDS) was employed for estimation of intrinsic dielectric loss of Zr0.8Sn0.2TiO4 (ZST) ceramics. Single-phase ZST dielectric resonators (DRs) with various synthesis parameters and, consequently, different extrinsic losses, were prepared by conventional ceramic technology. Even though the DRs exhibit a similar microstructure, their quality factor (Q is the inverse of dielectric loss tangent) measured in microwave (MW) domain at 6 GHz varies between 2500 and 8400. On the other hand, it was found that the THz dielectric loss is less sensitive to the sample preparation. The intrinsic losses (Q × f ~60 THz) of the ZST ceramics have been derived from THz data.
Keywords: dielectric resonators; electroceramics; intrinsic loss; microwave dielectrics; terahertz time-domain spectroscopy; zirconium tin titanate.