Hydroxyapatite reinforced Ti6Al4V composites for load-bearing implants

Abstract

Titanium has been used in various biomedical applications; however, titanium exhibits poor wear resistance, and its bioinert surface slows osseointegration in vivo. In this study, directed energy deposition (DED)-based additive manufacturing (AM) was used to process hydroxyapatite (HA) reinforced Ti6Al4V (Ti64) composites to improve biocompatibility and wear resistance simultaneously. Electron micrographs of the composites revealed dense microstructures where HA was observed at the β-phase grain boundaries. Hardness increased by 57% and 71% for 2 and 3 wt.% HA in Ti64 composites, respectively. XRD analysis revealed no change in the phases with the addition of HA, when compared to the control. Tribological studies displayed an increase in contact resistance (CR) due to an in situ formed HA-based tribofilm, reduction in wear rate when testing in Dulbecco's Modified Eagle Medium (DMEM) with a ZrO₂ counter wear ball, <1% wear ball volume loss, and suppression of cohesive shear failure of the Ti matrix. Histomorphometric analysis from a rat distal femur study revealed an increase in the osteoid surface over the bone surface (OS/BS) for 3 wt.% HA composite over the control Ti64 from 9 ± 1% to 14 ± 1%. Additionally, from push-out testing, the shear modulus was observed to increase from 17 ± 3 MPa for control Ti64 to 32 ± 5 MPa for the 3 wt.% HA composite after 5-weeks in vivo. The present study demonstrates that the addition of HA in Ti64 can simultaneously improve bone tissue-implant response and wear resistance.

Keywords: Additive manufacturing; Directed energy deposition; Hydroxyapatite; Ti6Al4V; Wear resistance.