Polyhydroxybutyrate (PHB) is a bio-based, biodegradable and commercially used polymer, which in its native form is unfortunately not generally applicable. A widely used technique to adapt polymers to a wider range of applications is the surface modification with amorphous hydrogenated carbon (a-C:H) layers, realized by plasma-enhanced chemical vapor deposition (PE-CVD). However, this process creates intrinsic stress in the layer-polymer system which can even lead to full layer failure. The aim of this study was to investigate how the carbon layer is affected when the basic polymer film to be coated can follow the stress and bend (single side attachment) and when it cannot do so because it is firmly clamped (full attachment). For both attachment methods, the a-C:H layers were simultaneously deposited on PHB samples. Ex-situ characterization was performed using a scanning electron microscope (SEM) for surface morphology and contact angle (CA) measurements for wettability. In addition, the stress prevailing in the layer was calculated using the Stoney equation. Diffuse reflectance infrared Fourier transform spectroscopy (DRIFT) measurements were used to investigate the chemical composition of the coating surface.
Keywords: a-C:H layers; biopolymer polyhydroxybutyrate (PHB); chemical surface environment; gradual film deposition; stress release phenomena.