A single step ultrasound-assisted nitrocellulose synthesis from microcrystalline cellulose

Ultrason Sonochem. 2021 Apr:72:105453. doi: 10.1016/j.ultsonch.2020.105453. Epub 2020 Dec 27.

Authors

Daniel Santos¹, Gabrielle D Iop¹, Cezar A Bizzi¹, Paola A Mello¹, Marcia F Mesko², Fernanda P Balbinot², Erico M M Flores³

Affiliations

¹ Department of Chemistry, Universidade Federal de Santa Maria, 97105-900 Santa Maria, RS, Brazil.
² Center of Chemistry, Pharmaceutical and Food Sciences, Universidade Federal de Pelotas, 96160-000 Pelotas, RS, Brazil.
³ Department of Chemistry, Universidade Federal de Santa Maria, 97105-900 Santa Maria, RS, Brazil. Electronic address: ericommf@gmail.com.

Abstract

Nitrocellulose is a nitrated cellulose polymer with a broad application in industry. Depending on the nitrogen content, this polymer can be used for manufacturing explosives, varnishes, clothes, and films, being considered a product of high value-added. In this work, the use of ultrasound was investigated for the intensification of nitrocellulose synthesis from microcrystalline cellulose. The ultrasound-assisted nitrocellulose synthesis (UANS) was carried out using several ultrasound systems, such as baths and cup horns, allowing the evaluation of the frequency (from 20 to 130 kHz) and delivered power (from 23 to 134 W dm^-3) to the reaction medium. The following parameters were evaluated: acid mixture (H₂SO₄, H₃PO₄, CH₂O₂ or CH₃COOH with HNO₃, 2 to 14.4 mol L^-1), ultrasound amplitude (10 to 70%) and reaction time (5 to 50 min). Better nitrocellulose yield (nitrogen content of 12.5% was obtained from 1 g of microcrystalline cellulose employing a cup horn system operating at 20 kHz, 750 W of nominal power with 60% of amplitude, 25 mL of acid solution (13.6 mL of 18.4 mol L^-1 H₂SO₄ + 9.2 mL of 14.4 mol L^-1 HNO₃ + 2.2 mL H₂O), at 30 °C for 30 min. At silent conditions (mechanical stirring ranging from 100 to 500 rpm), the nitrogen content was lower than 11.8% which demonstrate the ultrasound effects for nitrocellulose synthesis.

Keywords: Cellulose valorization; Process intensification; Ultrasound energy.