Goethite is a naturally anisotropic, antiferromagnetic iron oxide. Following its atomic structure, crystals grow into a fine needle shape that has interesting properties in a magnetic field. The needles align parallel to weak magnetic fields and perpendicular when subjected to high fields. We synthesized goethite nanorods with lengths between 200 nm and 650 nm in a two-step process. In a first step we synthesized precursor particles made of akaganeite (β-FeOOH) rods from iron(III)chloride. The precursors were then treated in a hydrothermal reactor under alkaline conditions with NaOH and polyvinylpyrrolidone (PVP) to form goethite needles. The aspect ratio was tunable between 8 and 15, based on the conditions during hydrothermal treatment. The orientation of these particles in a magnetic field was investigated by small angle X-ray scattering (SAXS). We observed that the field strength required to trigger a reorientation is dependent on the length and aspect ratio of the particles and could be shifted from 85 mT for the small particles to about 147 mT for the large particles. These particles could provide highly interesting magnetic properties to nanocomposites, that could then be used for sensing applications or membranes.
Keywords: akaganeite; anisotropy; goethite; hydrothermal; orientation; particle synthesis.