A performance mapping of GNP/epoxy composites was developed according to their electromechanical and electrothermal properties for applications as strain sensors and Joule heaters. To achieve this purpose, a deep theoretical and experimental study of the thermal and electrical conductivity of nanocomposites has been carried out, determining the influence of both nanofiller content and sonication time. Concerning dispersion procedure, at lower contents, higher sonication times induce a decrease of thermal and electrical conductivity due to a more prevalent GNP breakage effect. However, at higher GNP contents, sonication time implies an enhancement of both electrical and thermal properties due to a prevalence of exfoliating mechanisms. Strain monitoring tests indicate that electrical sensitivity increases in an opposite way than electrical conductivity, due to a higher prevalence of tunneling mechanisms, with the 5 wt.% specimens being those with the best results. Moreover, Joule heating tests showed the dominant role of electrical mechanisms on the effectiveness of resistive heating, with the 8 wt.% GNP samples being those with the best capabilities. By taking the different functionalities into account, it can be concluded that 5 wt.% samples with 1 h sonication time are the most balanced for electrothermal applications, as shown in a radar chart.
Keywords: carbon nanotubes; electrical properties; joule heating; strain sensing; thermal properties.