The wear resistance of diffusion coatings in conditions of specific pressures of 3, 7 and 10 MPa was studied. The boride coatings were prepared by means of diffusion methods using C45 steel as the substrate material. Research on the microstructure and redistribution of chemical elements on wear surface of a borided layer was carried out. It was found that the boride coatings should be used under a specific pressure of 7 MPa. It was found that the wear of friction couple coating of steel C45 under specific pressure of 3 MPa proceeds according to the oxidation wear mechanism, while under specific pressures of 7 and 10 MPa the abrasive wear prevails. The wear-induced segregation of atoms in coatings was studied using secondary mass-spectroscopy method (SIMS). Increased C, O, and B concentrations were noticed at the wear surface on depth from 50 to 2000 Å. The secondary wear-induced structure formation on the wear surface resulted in high wear resistance of diffusion borided coatings.
Keywords: borided coating; segregation; wear; wear mechanism.