The development of short-wave infrared (SWIR) photonics based on GeSn alloys is of high technological interest for many application fields, such as the Internet of things or pollution monitoring. The manufacture of crystalline GeSn is a major challenge, mainly because of the low miscibility of Ge and Sn. The use of embedded GeSn nanocrystals (NCs) by magnetron sputtering is a cost-effective and efficient method to relax the growth conditions. We report on the use of GeSn/SiO2 multilayer deposition as a way to control the NC size and their insulation. The in situ prenucleation of NCs during deposition was followed by ex situ rapid thermal annealing. The nanocrystallization of 20×(11nm_Ge0.865Sn0.135/1.5nm_SiO2) multilayers leads to formation of GeSn NCs with ∼16% Sn concentration and ∼9 nm size. Formation of GeSn domes that are vertically correlated contributes to the nanocrystallization process. The absorption limit of ∼0.4 eV in SWIR found by ellipsometry is in agreement with the spectral photosensitivity. The ITO/20×(GeSn NC/SiO2)/p-Si/Al diodes show a maximum value of the SWIR photosensitivity at a reverse voltage of 0.5 V, with extended sensitivity to wavelengths longer than 2200 nm. The multilayer diodes have higher photocurrent efficiency compared to diodes based on a thick monolayer of GeSn NCs.
Keywords: GeSn alloy; GeSn heterojunction diode; GeSn/SiO2 multilayers on Si; SWIR photosensitivity; magnetron sputtering; nanocomposite; nanocrystals.