The unsatisfactory cycle life of nickel-based cathodes hinders the widespread commercial usage of nickel-zinc (Ni-Zn) batteries. The most frequently used methods to improve the cycle life of Ni-based cathodes are usually complicated and/or involve using organic solvents and high energy consumption. A facile process based on the hydrolysis-induced exchange of the cobalt-based metal-organic framework (Co-MOF) was developed to prepare aluminum (Al)-doped cobalt-nickel double hydroxides (Al-CoNiDH) on a carbon cloth (CC). The entire synthesis process is highly efficient, energy-saving, and has a low negative impact on the environment. Compared to undoped cobalt-nickel double hydroxide (Al-CoNiDH-0%), the as-prepared Al-CoNiDH as the electrode material displays a remarkably improved cycling stability because the Al-doping successfully depresses the transition in the crystal phase and microstructure during the long cycling. Benefiting from the improved performance of the optimal Al-CoNiDH electrode (Al-CoNiDH-5% electrode), the as-constructed aqueous Ni-Zn battery with Al-CoNiDH-5% as the cathode (Al-CoNiDH-5%//Zn) displays more than 14% improvement in the cycle life relative to the Al-CoNiDH-0%//Zn battery. Moreover, this Al-CoNiDH-5%//Zn battery achieves a high specific capacity (264 mAh g-1), good rate capability (72.4% retention at a 30-fold higher current), high electrochemical energy conversion efficiency, superior fast-charging ability, and strong capability of reversible switching between fast charging and slow charging. Furthermore, the as-assembled quasi-solid-state Al-CoNiDH-5%//Zn battery exhibits a decent electrochemical performance and satisfactory flexibility.
Keywords: Al doping; Cathode; Cycle life; Hydroxide; Ni-Zn battery.
Copyright © 2020 Elsevier Inc. All rights reserved.