The present work is focused on the synthesis of CoCrFeMnNi high entropy alloy (HEA) interstitially alloyed with nitrogen via powder metallurgy routes. Using a simple method, nitrogen was introduced to the HEA from the protective N2 gas atmosphere during mechanical alloying (MA) processing. The lattice parameter and amount of nitrogen in HEA were observed to be linearly proportional to the milling duration. The limited solubility of nitrogen in the main face centered cubic (FCC) phase resulted in the in-situ formation of nitrides and, accordingly, significant increase in the hardness values. It has been shown that fabrication of such nitrogen-doped HEA bulk materials can be conveniently achieved by a simple combination of MA + spark plasma sintering processes, without the need for adding nitrogen from other sources.
Keywords: interstitial; metallurgy; microstructure; multi-principal element alloys; powder technology.